Magnetic tape having controlled surface properties of the magnetic layer

ABSTRACT

A magnetic tape includes a non-magnetic support; a non-magnetic layer including non-magnetic powder and a binder on the non-magnetic support; and a magnetic layer including ferromagnetic powder and a binder on the non-magnetic layer. The total thickness of the non-magnetic layer and the magnetic layer is less than or equal to 0.60 μm. The magnetic layer includes a timing-based servo pattern, and the logarithmic decrement acquired by a pendulum viscoelasticity test performed regarding the surface of the magnetic layer is less than or equal to 0.050.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims priority under 35 U.S.C 119 to Japanese Patent Application No. 2016-124933 filed on Jun. 23, 2016. The above application is hereby expressly incorporated by reference, in its entirety.

BACKGROUND OF THE INVENTION 1. Field of the Invention

The present invention relates to a magnetic tape and a magnetic tape device.

2. Description of the Related Art

Magnetic recording media are divided into tape-shaped magnetic recording media and disk-shaped magnetic recording media, and tape-shaped magnetic recording media, that is, magnetic tapes (hereinafter, also simply referred to as “tapes”) are mainly used for data storage such as data back-up or archive. The recording of information into magnetic tape is normally performed by recording a magnetic signal on a data band of the magnetic tape. Accordingly, data tracks are formed in the data band.

An increase in recording capacity (high capacity) of the magnetic tape is required in accordance with a great increase in information content in recent years. As means for realizing high capacity, a technology of disposing the larger amount of data tracks in a width direction of the magnetic tape by narrowing the width of the data track to increase recording density is used.

However, when the width of the data track is narrowed and the recording and/or reproduction of magnetic signals is performed by allowing the running of the magnetic tape in a magnetic tape device (normally referred to as a “drive”), it is difficult that a magnetic head correctly follows the data tracks in accordance with the position change of the magnetic tape in the width direction, and errors may easily occur at the time of recording and/or reproduction. Thus, as means for preventing occurrence of such errors, a system using a head tracking servo using a servo signal (hereinafter, referred to as a “servo system”) has been recently proposed and practically used (for example, see U.S. Pat. No. 5,689,384A).

SUMMARY OF THE INVENTION

In a magnetic servo type servo system among the servo systems, a servo pattern is formed in a magnetic layer of a magnetic tape, and this servo pattern is magnetically read to perform head tracking. More specific description is as follows.

First, a servo head reads a servo pattern formed in a magnetic layer (that is, reproduces a servo signal). A position of a magnetic head of the magnetic tape in a width direction is controlled in accordance with values (will be described later specifically) obtained by reading the servo pattern. Accordingly, when running the magnetic tape in the magnetic tape device for recording and/or reproducing a magnetic signal (information), it is possible to increase an accuracy of the position of the magnetic head following the data track, even when the position of the magnetic tape is changed in the width direction with respect to the magnetic head. By doing so, it is possible to correctly record information on the magnetic tape and/or correctly reproduce information recorded on the magnetic tape.

As the magnetic servo type servo system described above, a timing-based servo type system is widely used in recent years. In a timing-based servo type servo system (hereinafter, referred to as a “timing-based servo system”), a plurality of servo patterns having two or more different shapes are formed in a magnetic layer, and a position of a servo head is recognized by an interval of time when the servo head has read the two servo patterns having different shapes and an interval of time when the servo head has read two servo patterns having the same shapes. The position of the magnetic head of the magnetic tape in the width direction is controlled based on the position of the servo head recognized as described above.

Meanwhile, the magnetic tape is normally used to be accommodated and circulated in a magnetic tape cartridge. In order to increase recording capacity for 1 reel of the magnetic tape cartridge, it is desired to increase total length of the magnetic tape accommodated in 1 reel of the magnetic tape cartridge. In order to increase the recording capacity, it is necessary that the magnetic tape is thinned (hereinafter, referred to as “thinning”). As one method of thinning the magnetic tape, a method of decreasing the total thickness of a non-magnetic layer and a magnetic layer of a magnetic tape including the non-magnetic layer and the magnetic layer on a non-magnetic support in this order is used.

In consideration of these circumstances, the inventors have studied the application of a magnetic tape having a decreased total thickness of a non-magnetic layer and a magnetic layer to a timing-based servo system. However, in such studies, it was clear that, a phenomenon which was not known in the related art occurred, in which an output of a servo signal reproduced by a servo head is decreased compared to that in an initial running stage (hereinafter, also referred to as an “output decrease of a servo signal”) occurs, when a head tracking is continuously performed while causing the magnetic tape to run in a timing-based servo system, in a magnetic tape having the total thickness of a non-magnetic layer and a magnetic layer equal to or smaller than 0.60 μm. The output decrease of a servo signal causes a decrease in an accuracy of the position of the magnetic head following the data track in the timing-based servo system (hereinafter, referred to as a “head positioning accuracy”). Therefore, it is necessary that the output decrease of a servo signal is prevented, in order to more correctly record information to the magnetic tape and/or more correctly reproduce the information recorded in the magnetic tape by using the timing-based servo system.

Therefore, an object of the invention is to prevent an output decrease of a servo signal of a timing-based servo system, in a magnetic tape having the total thickness of a non-magnetic layer and a magnetic layer equal to or smaller than 0.60 μm.

According to one aspect of the invention, there is provided a magnetic tape comprising: a non-magnetic support; a non-magnetic layer including non-magnetic powder and a binder on the non-magnetic support; and a magnetic layer including ferromagnetic powder and a binder on the non-magnetic layer, in which the total thickness of the non-magnetic layer and the magnetic layer is equal to or smaller than 0.60 μm, the magnetic layer includes a timing-based servo pattern, and logarithmic decrement acquired by a pendulum viscoelasticity test performed regarding the surface of the magnetic layer is equal to or smaller than 0.050.

The “timing-based servo pattern” of the invention and the specification is a servo pattern with which the head tracking of the timing-based servo system can be performed. The timing-based servo system is as described above. The servo pattern with which the head tracking of the timing-based servo system can be performed, is formed in the magnetic layer by a servo pattern recording head (also referred to as a “servo write head”) as a plurality of servo patterns having two or more different shapes. As an example, the plurality of servo patterns having two or more different shapes are continuously disposed at regular intervals for each of the plurality of servo patterns having the same shapes. As another example, different types of the servo patterns are alternately disposed. The same shapes of the servo patterns do not only mean the completely same shape, and a shape error occurring due to a device such as a servo write head or the like is allowed. The shapes of the servo pattern with which the head tracking of the timing-based servo system can be performed and the disposition thereof in the magnetic layer are well known and specific aspect thereof will be described later. Hereinafter, the timing-based servo pattern is also simply referred to as a servo pattern. In the specification, as heads, a “servo write head”, a “servo head”, and a “magnetic head” are disclosed. The servo write head is a head which performs recording of a servo signal as described above (that is, formation of a servo pattern). The servo head is a head which performs reproduction of the servo signal (that is, reading of the servo pattern), and the magnetic head is a head which performs recording and/or reproduction of information.

In one aspect, the logarithmic decrement is 0.010 to 0.050.

In one aspect, the logarithmic decrement is 0.010 to 0.040.

In one aspect, in the magnetic tape, the total thickness of the non-magnetic layer and the magnetic layer is 0.20 μm to 0.60 μm.

According to another aspect of the invention, there is provided a magnetic tape device comprising: the magnetic tape described above; a magnetic head; and a servo head.

According to one aspect of the invention, it is possible to provide a magnetic tape in which the total thickness of a non-magnetic layer and a magnetic layer is equal to or smaller than 0.60 μm, a servo pattern is formed in a magnetic layer, and an output decrease of a servo signal of a timing-based servo system is prevented, and a magnetic tape device which records and/or reproduces a magnetic signal to the magnetic tape.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows an example of disposition of data bands and servo bands.

FIG. 2 shows a servo pattern disposition example of a linear-tape-open (LTO) Ultrium format tape.

FIG. 3 is an explanatory diagram of a measurement method of logarithmic decrement.

FIG. 4 is an explanatory diagram of the measurement method of logarithmic decrement.

FIG. 5 is an explanatory diagram of the measurement method of logarithmic decrement.

FIG. 6 shows an example (step schematic view) of a specific aspect of a magnetic tape manufacturing step.

DESCRIPTION OF THE PREFERRED EMBODIMENTS Magnetic Tape

According to one aspect of the invention, there is provided a magnetic tape including: a non-magnetic support; a non-magnetic layer including non-magnetic powder and a binder on the non-magnetic support; and a magnetic layer including ferromagnetic powder and a binder on the non-magnetic layer, in which the total thickness of the non-magnetic layer and the magnetic layer is equal to or smaller than 0.60 μm, the magnetic layer includes a timing-based servo pattern, and logarithmic decrement acquired by a pendulum viscoelasticity test performed regarding the surface of the magnetic layer (hereinafter also simply referred to as “logarithmic decrement”) is equal to or smaller than 0.050.

Hereinafter, the magnetic tape described above will be described more specifically. The following description contains surmise of the inventors. The invention is not limited by such surmise. In addition, hereinafter, the examples are described with reference to the drawings. However, the invention is not limited to such exemplified aspects.

Timing-Based Servo Pattern

The magnetic tape includes a timing-based servo pattern in the magnetic layer. The timing-based servo pattern is the servo pattern described above. In a magnetic tape used in a linear recording system which is widely used as a recording system of the magnetic tape device, for example, a plurality of regions (referred to as “servo bands”) where servo patterns are formed are normally present in the magnetic layer along a longitudinal direction of the magnetic tape. A region interposed between two servo bands is referred to as a data band. The recording of magnetic signals (information) is performed on the data band and a plurality of data tracks are formed in each data band along the longitudinal direction.

FIG. 1 shows an example of disposition of data bands and servo bands. In FIG. 1, a plurality of servo bands 10 are disposed to be interposed between guide bands 12 in a magnetic layer of a magnetic tape 1. A plurality of regions 11 each of which is interposed between two servo bands are data bands. The servo pattern is a magnetized region and is formed by magnetizing a specific region of the magnetic layer by a servo write head. The region magnetized by the servo write head (position where a servo pattern is formed) is determined by standards. For example, in a LTO Ultrium format tape which is based on a local standard, a plurality of servo patterns tilted in a tape width direction as shown in FIG. 2 are formed on a servo band when manufacturing a magnetic tape. Specifically, in FIG. 2, a servo frame SF on the servo band 10 is configured with a servo sub-frame 1 (SSF1) and a servo sub-frame 2 (SSF2). The servo sub-frame 1 is configured with an A burst (in FIG. 2, reference numeral A) and a B burst (in FIG. 2, reference numeral B). The A burst is configured with servo patterns A1 to A5 and the B burst is configured with servo patterns B1 to B5. Meanwhile, the servo sub-frame 2 is configured with a C burst (in FIG. 2, reference numeral C) and a D burst (in FIG. 2, reference numeral D). The C burst is configured with servo patterns C1 to C4 and the D burst is configured with servo patterns D1 to D4. Such 18 servo patterns are disposed in the sub-frames in the arrangement of 5, 5, 4, 4, as the sets of 5 servo patterns and 4 servo patterns, and are used for recognizing the servo frames. FIG. 2 shows one servo frame for description. However, in practice, in a magnetic layer of the magnetic tape in which a head tracking is performed in a timing-based servo system, a plurality of servo frames are disposed in each servo band in a running direction. In FIG. 2, an arrow shows the running direction. For example, a LTO Ultrium format tape generally includes 5,000 or more servo frames per a tape length of 1 m, in each servo band of the magnetic layer. The servo head sequentially reads the servo patterns in the plurality of servo frames, while coming into contact with and sliding on the surface of the magnetic layer of the running magnetic tape.

In the timing-based servo system, a position of a servo head is recognized based on an interval of time when the servo head has read the two servo patterns (reproduced servo signals) having different shapes and an interval of time when the servo head has read two servo patterns having the same shapes. The time interval is normally obtained as a time interval of a peak of a reproduced waveform of a servo signal. For example, in the aspect shown in FIG. 2, the servo pattern of the A burst and the servo pattern of the C burst are servo patterns having the same shapes, and the servo pattern of the B burst and the servo pattern of the D burst are servo patterns having the same shapes. The servo pattern of the A burst and the servo pattern of the C burst are servo patterns having the shapes different from the shapes of the servo pattern of the B burst and the servo pattern of the D burst. An interval of the time when the two servo patterns having different shapes are read by the servo head is, for example, an interval between the time when any servo pattern of the A burst is read and the time when any servo pattern of the B burst is read. An interval of the time when the two servo patterns having the same shapes are read by the servo head is, for example, an interval between the time when any servo pattern of the A burst is read and the time when any servo pattern of the C burst is read. The timing-based servo system is a system supposing that occurrence of a deviation of the time interval is due to a position change of the magnetic tape in the width direction, in a case where the time interval is deviated from the set value. The set value is a time interval in a case where the magnetic tape runs without occurring the position change in the width direction. In the timing-based servo system, the magnetic head is moved in the width direction in accordance with a degree of the deviation of the obtained time interval from the set value. Specifically, as the time interval is greatly deviated from the set value, the magnetic head is greatly moved in the width direction. This point is applied to not only the aspect shown in FIG. 1 and FIG. 2, but also to entire timing-based servo systems. When recording and reproducing magnetic signals (information) by the magnetic head by causing the magnetic tape to run in the magnetic tape device using the timing-based servo system, a decrease in output of a servo signal while continuously reading the servo pattern (continuously reproducing the servo signal) by the servo head causes a decrease in a measurement accuracy of the time interval. As a result, while the running is continuously performed, a head positioning accuracy is decreased. In regards to this point, in the studies of the inventors, it was found that the output decrease of the servo signal significantly occurs in the magnetic tape having the total thickness of the non-magnetic layer and the magnetic layer equal to or smaller than 0.60 μm. The inventors have thought that a main reason of the output decrease of the servo signal is attached materials derived from the magnetic tape attached to a servo write head, while a plurality of servo patterns are sequentially formed in the magnetic layer while the servo write head comes into contact with and slide on the surface of the magnetic layer of the magnetic tape. The inventors have surmised that, as a result of deterioration of servo pattern forming ability of the servo write head due to the effect of the attached materials, a magnetic force of the servo pattern formed is gradually deteriorated, while the servo patterns are continuously formed. It is thought that in the magnetic layer having the servo patterns formed as described above, the output of a servo signal is decreased, while the servo patterns are continuously read by the servo head (servo signals are continuously reproduced). The inventors have surmised that, a reason of the occurrence of such a phenomenon in the magnetic tape having the total thickness of the non-magnetic layer and the magnetic layer equal to or smaller than 0.60 μm may be a contact state between the servo write head and the surface of the magnetic layer of the magnetic tape which is different from that of the magnetic tape having the total thickness of the non-magnetic layer and the magnetic layer exceeding 0.60 μm. However, this is merely a surmise. With respect this, as a result of the intensive studies of the inventors, it was clear that the output decrease of the servo signal of the magnetic tape having the total thickness of the non-magnetic layer and the magnetic layer equal to or smaller than 0.60 μm can be prevented by setting the logarithmic decrement to be equal to or smaller than 0.050. The surmise of the inventors regarding this point will be described later.

Logarithmic Decrement

The logarithmic decrement acquired by a pendulum viscoelasticity test performed regarding the surface of the magnetic layer of the magnetic tape is equal to or smaller than 0.050. Accordingly, it is possible to prevent the output decrease of the servo signal in the magnetic tape having the total thickness of the non-magnetic layer and the magnetic layer equal to or smaller than 0.60 μm. From a viewpoint of further preventing the output decrease of the servo signal, the logarithmic decrement is preferably equal to or smaller than 0.045 and more preferably equal to or smaller than 0.040. Meanwhile, from a viewpoint of preventing the output decrease of the servo signal, it is preferable that the logarithmic decrement is low, and therefore, the lower limit value is not particularly limited. The logarithmic decrement can be, for example, equal to or greater than 0.010 or equal to or greater than 0.015. However, the logarithmic decrement may be smaller than the exemplified value. A specific aspect of a method for adjusting the logarithmic decrement will be described later. In addition, in the invention and the specification, the “surface of the magnetic layer” is identical to the surface of the magnetic tape on the magnetic layer side.

In the invention and the specification, the logarithmic decrement is a value acquired by the following method.

FIG. 3 to FIG. 5 are explanatory diagrams of a measurement method of the logarithmic decrement. Hereinafter, the measurement method of the logarithmic decrement will be described with reference to the drawings. However, the aspect shown in the drawing is merely an example and the invention is not limited thereto.

A measurement sample 100 is cut out from the magnetic tape which is a measurement target. The cut-out measurement sample 100 is placed on a substrate 103 so that a measurement surface (surface of the magnetic layer) faces upwards, in a sample stage 101 in a pendulum viscoelasticity tester, and the measurement sample is fixed by fixing tapes 105 in a state where obvious wrinkles which can be visually confirmed are not generated.

A pendulum-attached columnar cylinder edge 104 (diameter of 4 mm) having mass of 13 g is loaded on the measurement surface of the measurement sample 100 so that a long axis direction of the cylinder edge becomes parallel to a longitudinal direction of the measurement sample 100. An example of a state in which the pendulum-attached columnar cylinder edge 104 is loaded on the measurement surface of the measurement sample 100 as described above (state seen from the top) is shown in FIG. 3. In the aspect shown in FIG. 3, a holder and temperature sensor 102 is installed and a temperature of the surface of the substrate 103 can be monitored. However, this configuration is not essential. In the aspect shown in FIG. 3, the longitudinal direction of the measurement sample 100 is a direction shown with an arrow in the drawing, and is a longitudinal direction of a magnetic tape from which the measurement sample is cut out. In addition, the description regarding angles such as “parallel” in the specification includes a range of errors allowed in the technical field of the invention. For example, this means that the error is in a range within less than ±10° from an exact angle, and the error from the exact angle is preferably equal to or smaller than 5° and more preferably equal to or smaller than 3°. In addition, as a pendulum 107 (see FIG. 4), a pendulum formed of a material having properties of being adsorbed to a magnet such as metal or an alloy is used.

The temperature of the surface of the substrate 103 on which the measurement sample 100 is placed is set to 80° C. by increasing the temperature at a rate of temperature increase equal to or lower than 5° C./min (arbitrary rate of temperature increase may be set, as long as it is equal to or lower than 5° C./min), and the pendulum movement is started (induce initial vibration) by releasing adsorption between the pendulum 107 and a magnet 106. An example of a state of the pendulum 107 which performs the pendulum movement (state seen from the side) is shown in FIG. 4. In the aspect shown in FIG. 4, in the pendulum viscoelasticity tester, the pendulum movement is started by stopping (switching off) the electricity to the magnet (electromagnet) 106 disposed on the lower side of the sample stage to release the adsorption, and the pendulum movement is stopped by restarting (switching on) the electricity to the electromagnet to cause the pendulum 107 to be adsorbed to the magnet 106. As shown in FIG. 4, during the pendulum movement, the pendulum 107 reciprocates the amplitude. From a result obtained by monitoring displacement of the pendulum with a displacement sensor 108 while the pendulum reciprocates the amplitude, a displacement-time curve in which a vertical axis indicates the displacement and a horizontal axis indicates the elapsed time is obtained. An example of the displacement-time curve is shown in FIG. 5. FIG. 5 schematically shows correspondence between the state of the pendulum 107 and the displacement-time curve. The rest (adsorption) and the pendulum movement are repeated at a regular measurement interval, the logarithmic decrement Δ (no unit) is acquired from the following Expression by using a displacement-time curve obtained in the measurement interval after 10 minutes or longer (may be arbitrary time, as long as it is 10 minutes or longer) has elapsed, and this value is set as logarithmic decrement of the surface of the magnetic layer of the magnetic tape. The adsorption time of the first adsorption is set as 1 second or longer (may be arbitrary time, as long as it is 1 second or longer), and the interval between the adsorption stop and the adsorption start is set as 6 seconds or longer (may be arbitrary time, as long as it is 6 seconds or longer). The measurement interval is an interval of the time from the adsorption start and the nest adsorption start. In addition, humidity of an environment in which the pendulum movement is performed, may be arbitrary relative humidity, as long as the relative humidity is in a range of 40% to 70%.

$\Delta = \frac{{\ln\left( \frac{A_{1}}{A_{2\;}} \right)} + {\ln\left( \frac{A_{2}}{A_{3}} \right)} + {\ldots\mspace{14mu}{\ln\left( \frac{A_{n}}{A_{n + 1}} \right)}}}{n}$

In the displacement-time curve, an interval between a point of the minimum displacement and a point of the next minimum displacement is set as a period of a wave. n indicates the number of waves included in the displacement-time curve in the measurement interval, and An indicates the minimum displacement and maximum displacement of the n-th wave. In FIG. 5, an interval between the minimum displacement of the n-th wave and the next minimum displacement is shown as Pn (for example, P₁ regarding the first wave, P₂ regarding the second wave, and P₃ regarding the third wave). In the calculation of the logarithmic decrement, a difference (in Expression, A_(n+1), and in the displacement-time curve shown in FIG. 5, A₄) between the minimum displacement and the maximum displacement appearing after the n-th wave is also used, but a part where the pendulum 107 stops (adsorption) after the maximum displacement is not used in the counting of the number of waves. In addition, a part where the pendulum 107 stops (adsorption) before the maximum displacement is not used in the counting of the number of waves, either. Accordingly, the number of waves is 3 (n=3) in the displacement-time curve shown in FIG. 5.

In regards to the logarithmic decrement, the inventors have considered as follows. However, the following description is merely a surmise and the invention is not limited thereto.

In the intensive studies of the inventors, it was found that, a phenomenon in which an output of a servo signal reproduced by a servo head is decreased compared to that in an initial running stage (output decrease of a servo signal) occurs, when a head tracking is continuously performed while causing the surface of the magnetic layer of the magnetic tape having the total thickness of a non-magnetic layer and a magnetic layer equal to or smaller than 0.60 μm to come into contact with and slide on the servo head, in the timing-based servo system. The inventors have surmised that a main reason of the output decrease of the servo signal is that attached materials derived from the magnetic tape is attached to a servo write head, while a plurality of servo patterns are sequentially formed in the magnetic layer while the servo write head comes into contact with and slides on the surface of the magnetic layer, and servo pattern forming ability of the servo write head is deteriorated due to the effect of the attached materials. The inventors have surmised that the reason of the effect of the attached materials being significant in the magnetic tape having the total thickness of the non-magnetic layer and the magnetic layer equal to or smaller than 0.60 μm is the contact state with the servo write head of the magnetic tape which is different from that of a magnetic tape having the total thickness of the non-magnetic layer and the magnetic layer exceeding 0.60 μm.

Therefore, the inventors have made further intensive research regarding the reason of the generation of the attached materials. As a result, the inventors have newly found that the logarithmic decrement may be an index of the amount of the attached materials derived from the magnetic tape which are attached and collected on the servo write head, and by setting the value thereof to be equal to or smaller than 0.050, it is possible to prevent the output decrease of the servo signal.

The inventors have thought that a component to be the attached materials derived from the magnetic tape include a viscous component separated from the magnetic tape, when the servo write head and the surface of the magnetic layer come into contact with each other. The details of the viscous component are not clear. However, the inventors have surmised that the viscous component may be derived from a resin used as a binder. Specific description is as follows.

As a binder, various resins can be used as will be described later in detail. The resin is a polymer (including a homopolymer or a copolymer) of two or more polymerizable compounds and generally also includes a component having a molecular weight which is smaller than an average molecular weight (hereinafter, referred to as a “binder component having a low molecular weight”). The inventors have thought that the binder component having a low molecular weight which separated from the magnetic tape and attached and collected on the servo write head, while the servo write head continuously comes into contact with and slides on the surface of the magnetic layer, in order to sequentially form a plurality of servo patterns in the magnetic layer, causes the output decrease of the servo signal, as a result. The inventors have surmised that, the binder component having a low molecular weight may have viscosity and the logarithmic decrement acquired by the pendulum viscoelasticity test may be an index of the amount of the attached materials attached and collected on the servo write head, while the servo write head continuously sequentially forms a plurality of servo patterns in the magnetic layer. In one aspect, the magnetic layer is formed by applying a magnetic layer forming composition including a curing agent in addition to ferromagnetic powder and a binder onto a non-magnetic support directly or with another layer interposed therebetween, and performing curing process. With the curing process here, it is possible to allow a curing reaction (crosslinking reaction) between the binder and the curing agent. However, the reason thereof is not clear, and the inventors have thought that the binder component having a low molecular weight may have poor reactivity regarding the curing reaction. Accordingly, the inventors have surmised that the binder component having a low molecular weight which hardly remains in the magnetic layer and is easily separated from the magnetic layer and attached to the servo write head may be one of reasons for that the binder component having a low molecular weight is easily attached and collected on the servo write head, while the servo write head continuously sequentially forms a plurality of servo patterns in the magnetic layer.

However, the above-mentioned description is merely a surmise of the inventors and the invention is not limited thereto.

Hereinafter, the magnetic tape described above will be described more specifically.

Magnetic Layer

Ferromagnetic Powder

The magnetic layer includes ferromagnetic powder and a binder. As the ferromagnetic powder, various powders normally used as ferromagnetic powder in the magnetic layer of a magnetic recording medium such as a magnetic tape can be used. It is preferable to use ferromagnetic powder having a small average particle size, from a viewpoint of improvement of recording density of the magnetic tape. From this viewpoint, ferromagnetic powder having an average particle size equal to or smaller than 50 nm is preferably used as the ferromagnetic powder. Meanwhile, the average particle size of the ferromagnetic powder is preferably equal to or greater than 10 nm, from a viewpoint of stability of magnetization.

An average particle sizes of the ferromagnetic powder is a value measured by the following method with a transmission electron microscope.

The ferromagnetic powder is imaged at a magnification ratio of 100,000 with a transmission electron microscope, and the image is printed on printing paper so that the total magnification becomes 500,000, to obtain an image of particles configuring the ferromagnetic powder. A target particle is selected from the obtained image of particles, an outline of the particle is traced with a digitizer, and a size of the particle (primary particle) is measured. The primary particle is an independent particle which is not aggregated.

The measurement described above is performed regarding 500 particles arbitrarily extracted. An arithmetical mean of the particle size of 500 particles obtained as described above is an average particle size of the ferromagnetic powder. As the transmission electron microscope, a transmission electron microscope H-9000 manufactured by Hitachi, Ltd. can be used, for example. In addition, the measurement of the particle size can be performed by well-known image analysis software, for example, image analysis software KS-400 manufactured by Carl Zeiss.

In the invention and the specification, the average particle size of the ferromagnetic powder and other powder is an average particle size obtained by the method described above, unless otherwise noted. The average particle size shown in Examples which will be described later is measured by using transmission electron microscope H-9000 manufactured by Hitachi, Ltd. as the transmission electron microscope, and image analysis software KS-400 manufactured by Carl Zeiss as the image analysis software.

As a method of collecting a sample powder such as ferromagnetic powder from the magnetic layer in order to measure the particle size, a method disclosed in a paragraph of 0015 of JP2011-048878A can be used, for example.

In the invention and the specification, (1) in a case where the shape of the particle observed in the particle image described above is a needle shape, a fusiform shape, or a columnar shape (here, a height is greater than a maximum long diameter of a bottom surface), the size (hereinafter, referred to as a “particle size”) of the particles configuring the powder such as ferromagnetic powder is shown as a length of a long axis configuring the particle, that is, a long axis length, (2) in a case where the shape of the particle is a planar shape or a columnar shape (here, a thickness or a height is smaller than a maximum long diameter of a plate surface or a bottom surface), the particle size is shown as a maximum long diameter of the plate surface or the bottom surface, and (3) in a case where the shape of the particle is a sphere shape, a polyhedron shape, or an unspecified shape, and the long axis configuring the particles cannot be specified from the shape, the particle size is shown as an equivalent circle diameter. The equivalent circle diameter is a value obtained by a circle projection method.

In addition, regarding an average acicular ratio of the powder, a length of a short axis, that is, a short axis length of the particles is measured in the measurement described above, a value of (long axis length/short axis length) of each particle is obtained, and an arithmetical mean of the values obtained regarding 500 particles is calculated. Here, in a case of (1), the short axis length as the definition of the particle size is a length of a short axis configuring the particle, in a case of (2), the short axis length is a thickness or a height, and in a case of (3), the long axis and the short axis are not distinguished, thus, the value of (long axis length/short axis length) is assumed as 1, for convenience.

In addition, in a case where the shape of the particle is specified, for example, in a case of definition of the particle size (1), the average particle size is an average long axis length, in a case of the definition (2), the average particle size is an average plate diameter, and an average plate ratio is an arithmetical mean of (maximum long diameter/thickness or height). In a case of the definition (3), the average particle size is an average diameter (also referred to as an average particle diameter).

As a preferred specific example of the ferromagnetic powder, ferromagnetic hexagonal ferrite powder can be used. An average particle size of the ferromagnetic hexagonal ferrite powder (average plate diameter) is preferably 10 nm to 50 nm and more preferably 20 nm to 50 nm, from a viewpoint of realizing high-density recording and stability of magnetization. For details of the ferromagnetic hexagonal ferrite powder, descriptions disclosed in paragraphs 0012 to 0030 of JP2011-225417A, paragraphs 0134 to 0136 of JP2011-216149A, and paragraphs 0013 to 0030 of JP2012-204726A can be referred to, for example.

As a preferred specific example of the ferromagnetic powder, ferromagnetic metal powder can also be used. An average particle size (average long axis length) of the ferromagnetic metal powder is preferably 10 nm to 50 nm and more preferably 20 nm to 50 nm, from a viewpoint of high-density recording and stability of magnetization. For details of the ferromagnetic metal powder, descriptions disclosed in paragraphs 0137 to 0141 of JP2011-216149A and paragraphs 0009 to 0023 of JP2005-251351A can be referred to, for example.

The content (filling percentage) of the ferromagnetic powder of the magnetic layer is preferably in a range of 50 to 90 mass % and more preferably in a range of 60 to 90 mass %. The components other than the ferromagnetic powder of the magnetic layer are at least a binder and one or more kinds of additives may be arbitrarily included. A high filling percentage of the ferromagnetic powder in the magnetic layer is preferable from a viewpoint of improvement recording density.

Binder and Curing Agent

The magnetic tape is a coating type magnetic tape, and the magnetic layer includes a binder. The binder is one or more kinds of resin. As the binder, various resins normally used as a binder of a coating type magnetic recording medium can be used. For example, as the binder, a resin selected from a polyurethane resin, a polyester resin, a polyamide resin, a vinyl chloride resin, an acrylic resin obtained by copolymerizing styrene, acrylonitrile, or methyl methacrylate, a cellulose resin such as nitrocellulose, an epoxy resin, a phenoxy resin, and a polyvinylalkylal resin such as polyvinyl acetal or polyvinyl butyral can be used alone or a plurality of resins can be mixed with each other to be used. Among these, a polyurethane resin, an acrylic resin, a cellulose resin, and a vinyl chloride resin are preferable. These resins may be a homopolymer or a copolymer. These resins can be used as the binder even in the non-magnetic layer and/or a back coating layer which will be described later. For the binder described above, description disclosed in paragraphs 0028 to 0031 of JP2010-24113A can be referred to. An average molecular weight of the resin used as the binder can be, for example, 10,000 to 200,000 as a weight-average molecular weight. The weight-average molecular weight of the invention and the specification is a value obtained by performing polystyrene conversion of a value measured by gel permeation chromatography (GPC). As the measurement conditions, the following conditions can be used. The weight-average molecular weight shown in Examples which will be described later is a value obtained by performing polystyrene conversion of a value measured under the following measurement conditions.

GPC device: HLC-8120 (manufactured by Tosoh Corporation)

Column: TSK gel Multipore HXL-M (manufactured by Tosoh Corporation, 7.8 mmID (inner diameter)×30.0 cm)

Eluent: Tetrahydrofuran (THF)

In addition, a curing agent can also be used together with a resin which can be used as the binder. As the curing agent, in one aspect, a thermosetting compound which is a compound in which a curing reaction (crosslinking reaction) proceeds due to heating can be used, and in another aspect, a photocurable compound in which a curing reaction (crosslinking reaction) proceeds due to light irradiation can be used. At least a part of the curing agent is included in the magnetic layer in a state of being reacted (crosslinked) with other components such as the binder, by proceeding the curing reaction in the magnetic layer forming step. The preferred curing agent is a thermosetting compound, polyisocyanate is suitable. For the details of polyisocyanate, descriptions disclosed in paragraphs 0124 and 0125 of JP2011-216149A can be referred to, for example. The amount of the curing agent can be, for example, 0 to 80.0 parts by mass with respect to 100.0 parts by mass of the binder in the magnetic layer forming composition, and is preferably 50.0 to 80.0 parts by mass, from a viewpoint of improvement of strength of each layer such as the magnetic layer.

Additive

The magnetic layer includes the ferromagnetic powder and the binder, and may include one or more kinds of additives, if necessary. As the additives, the curing agent described above is used as an example. In addition, examples of the additive which can be included in the magnetic layer include a non-magnetic filler, a lubricant, a dispersing agent, a dispersing assistant, an antibacterial agent, an antistatic agent, an antioxidant, and carbon black. As the additives, a commercially available product can be suitably selected and used according to desired properties.

Hereinafter, a non-magnetic filler which is one aspect of the additive will be described. However, the invention is not limited to the following aspect. The non-magnetic filler is identical to the non-magnetic powder. In addition, in the invention and the specification, the non-magnetic powder means an aggregate of a plurality of non-magnetic particles. The aggregate not only includes an aspect in which particles configuring the aggregate directly come into contact with each other, and also includes an aspect in which a binder and an additive is interposed between the particles. A term “particles” is also used for describing the powder. The same applies to various powders of the invention and the specification.

It is preferable that the magnetic layer includes one kind or two or more kinds of the non-magnetic filler. As the non-magnetic filler, a non-magnetic filler (hereinafter, referred to as a “projection formation agent”) which can function as a projection formation agent which forms projections suitably protruded from the surface of the magnetic layer, and a non-magnetic filler (hereinafter, referred to as an “abrasive”) which can function as an abrasive can be used. The projection formation agent is a component which can contribute to the control of friction properties of the surface of the magnetic layer. It is preferable that at least one of the projection formation agent and the abrasive is included in the magnetic layer of the magnetic tape, and it is preferable that both of them are included.

As the projection formation agent, various non-magnetic fillers normally used as a projection formation agent can be used. These may be inorganic substances or organic substances. In one aspect, from a viewpoint of homogenization of friction properties, particle size distribution of the projection formation agent is not polydispersion having a plurality of peaks in the distribution and is preferably monodisperse showing a single peak. From a viewpoint of availability of monodisperse particles, the non-magnetic filler is preferably powder of inorganic substances. Examples of the powder of inorganic substances include powder of metal oxide, metal carbonate, metal sulfate, metal nitride, metal carbide, and metal sulfide, and powder of inorganic oxide is preferable. The projection formation agent is more preferably colloidal particles and even more preferably inorganic oxide colloidal particles. In addition, from a viewpoint of availability of monodisperse particles, the inorganic oxide configuring the inorganic oxide colloidal particles are preferably silicon dioxide (silica). The inorganic oxide colloidal particles are more preferably colloidal silica (silica colloidal particles). The average particle size of the colloidal particles is a value obtained by a method disclosed in a paragraph 0015 of JP2011-048878A as a measurement method of an average particle diameter. In addition, in another aspect, the projection formation agent is preferably carbon black.

An average particle size of the projection formation agent is, for example, 30 to 300 nm and is preferably 40 to 200 nm.

Meanwhile, as the abrasive, powders of alumina (Al₂O₃), silicon carbide, boron carbide (B₄C), SiO₂, TiC chromium oxide (Cr₂O₃), cerium oxide, zirconium oxide (ZrO₂), iron oxide, diamond, and the like which are substances normally used as the abrasive of the magnetic layer can be used, and among these, alumina powder such as α-alumina and silicon carbide powder are preferable. In addition, regarding the particle size of the abrasive, a specific surface area which is an index of the particle size is, for example, equal to or greater than 14 m²/g, and is preferably 16 m²/g and more preferably 18 m²/g. Further, the specific surface area of the abrasive can be, for example, equal to or smaller than 40 m²/g. The specific surface area is a value obtained by a nitrogen adsorption method (also referred to as a Brunauer-Emmett-Teller (BET) 1 point method), and is a value measured regarding primary particles. Hereinafter, the specific surface area obtained by such a method is also referred to as a BET specific surface area.

In addition, from a viewpoint that the projection formation agent and the abrasive can exhibit the functions thereof in more excellent manner, the content of the projection formation agent of the magnetic layer is preferably 1.0 to 4.0 parts by mass and more preferably 1.5 to 3.5 parts by mass with respect to 100.0 parts by mass of the ferromagnetic powder. Meanwhile, the content of the abrasive in the magnetic layer is preferably 1.0 to 20.0 parts by mass, more preferably 3.0 to 15.0 parts by mass, and even more preferably 4.0 to 10.0 parts by mass with respect to 100.0 parts by mass of the ferromagnetic powder.

As an example of the additive which can be used in the magnetic layer including the abrasive, a dispersing agent disclosed in paragraphs 0012 to 0022 of JP2013-131285A can be used as a dispersing agent for improving dispersibility of the abrasive.

Non-Magnetic Layer

Next, the non-magnetic layer will be described. The magnetic tape may directly include a magnetic layer on a non-magnetic support, or may include a magnetic layer on a non-magnetic support with at least another layer interposed therebetween. Such another layer is preferably a non-magnetic layer including non-magnetic powder and a binder. The non-magnetic powder used in the non-magnetic layer may be inorganic substances or organic substances. In addition, carbon black and the like can be used. Examples of the inorganic substances include metal, metal oxide, metal carbonate, metal sulfate, metal nitride, metal carbide, and metal sulfide. The non-magnetic powder can be purchased as a commercially available product or can be manufactured by a well-known method. For details thereof, descriptions disclosed in paragraphs 0146 to 0150 of JP2011-216149A can be referred to. For carbon black which can be used in the non-magnetic layer, descriptions disclosed in paragraphs 0040 and 0041 of JP2010-24113A can be referred to. The content (filling percentage) of the non-magnetic powder of the non-magnetic layer is preferably in a range of 50 to 90 mass % and more preferably in a range of 60 to 90 mass %.

In regards to other details of a binder or additives of the non-magnetic layer, the well-known technology regarding the non-magnetic layer can be applied. In addition, in regards to the type and the content of the binder, and the type and the content of the additive, for example, the well-known technology regarding the magnetic layer can be applied.

The non-magnetic layer of the magnetic tape also includes a substantially non-magnetic layer including a small amount of ferromagnetic powder as impurities or intentionally, together with the non-magnetic powder. Here, the substantially non-magnetic layer is a layer having a residual magnetic flux density equal to or smaller than 10 mT, a layer having coercivity equal to or smaller than 7.96 kA/m (100 Oe), or a layer having a residual magnetic flux density equal to or smaller than 10 mT and coercivity equal to or smaller than 7.96 kA/m (100 Oe). It is preferable that the non-magnetic layer does not have a residual magnetic flux density and coercivity.

Non-Magnetic Support

Next, the non-magnetic support (hereinafter, also simply referred to as a “support”) will be described. As the non-magnetic support, well-known components such as polyethylene terephthalate, polyethylene naphthalate, polyamide, polyamide imide, aromatic polyamide subjected to biaxial stretching are used. Among these, polyethylene terephthalate, polyethylene naphthalate, and polyamide are preferable. Corona discharge, plasma treatment, easy-bonding treatment, or thermal treatment may be performed with respect to these supports in advance.

Back Coating Layer

The magnetic tape can also include a back coating layer including non-magnetic powder and a binder on a side of the non-magnetic support opposite to the side including the magnetic layer. The back coating layer preferably includes any one or both of carbon black and inorganic powder. In regards to the binder included in the back coating layer and various additives which can be arbitrarily included in the back coating layer, a well-known technology regarding the treatment of the magnetic layer and/or the non-magnetic layer can be applied.

Various Thickness

In the magnetic tape, the total thickness of the magnetic layer and the non-magnetic layer is equal to or smaller than 0.60 μm and preferably equal to or smaller than 0.50 μm, from a viewpoint of thinning the magnetic tape. In addition, the total thickness of the magnetic layer and the non-magnetic layer is, for example, equal to or greater than 0.10 μm or equal to or greater than 0.20 μm.

In the thicknesses of the non-magnetic support and each layer of the magnetic tape, the thickness of the non-magnetic support is preferably 3.00 to 4.50 μm.

A thickness of the magnetic layer can be optimized in accordance with saturation magnetization quantity of the magnetic head used, a head gap length, or a band of a recording signal. The thickness of the magnetic layer is normally 0.01 μm to 0.15 μm, and is preferably 0.02 μm to 0.12 μm and more preferably 0.03 μm to 0.10 μm, from a viewpoint of realizing recording at high density. The magnetic layer may be at least single layer, the magnetic layer may be separated into two or more layers having different magnetic properties, and a configuration of a well-known multilayered magnetic layer can be applied. A thickness of the magnetic layer in a case where the magnetic layer is separated into two or more layers is the total thickness of the layers.

The thickness of the non-magnetic layer is, for example, 0.10 to 0.55 μm and is preferably 0.10 to 0.50 μm.

A thickness of the back coating layer is preferably equal to or smaller than 0.90 μm and even more preferably in a range of 0.10 to 0.70 μm.

In addition, the total thickness of the magnetic tape is preferably equal to or smaller than 6.00 μm, more preferably equal to or smaller than 5.70 μm, and even more preferably equal to or smaller than 5.50 μm, from a viewpoint of improving recording capacity for 1 magnetic tape cartridge. Meanwhile, the total thickness of the magnetic tape is preferably equal to or greater than 1.00 μm, from a viewpoint of availability (handling properties) of the magnetic tape.

The thicknesses of various layers of the magnetic tape and the non-magnetic support can be acquired by a well-known film thickness measurement method. As an example, a cross section of the magnetic tape in a thickness direction is, for example, exposed by a well-known method of ion beams or microtome, and the exposed cross section is observed with a scan electron microscope. In the cross section observation, various thicknesses can be acquired as a thickness acquired at one position of the cross section in the thickness direction, or an arithmetical mean of thicknesses acquired at a plurality of positions of two or more positions, for example, two positions which are arbitrarily extracted. In addition, the thickness of each layer may be acquired as a designed thickness calculated according to the manufacturing conditions.

Measurement Method

Manufacturing of Magnetic Tape in which Servo Pattern is Formed

Preparation of Each Layer Forming Composition

Each composition for forming the magnetic layer, the non-magnetic layer, or the back coating layer normally includes a solvent, together with various components described above. As the solvent, organic solvents generally used for manufacturing a coating type magnetic recording medium can be used. Among those, from a viewpoint of solubility of the binder normally used in the coating type magnetic recording medium, each layer forming composition preferably includes one or more ketone solvents such as acetone, methyl ethyl ketone, methyl isobutyl ketone, diisobutyl ketone, cyclohexanone, isophorone, and tetrahydrofuran. The amount of the solvent of each layer forming composition is not particularly limited, and can be set to be the same as that of each layer forming composition of a typical coating type magnetic recording medium.

The steps of preparing each layer forming composition generally include at least a kneading step, a dispersing step, and a mixing step provided before and after these steps, if necessary. Each step may be divided into two or more stages. All of raw materials used in the invention may be added at an initial stage or in a middle stage of each step. In addition, each raw material may be separately added in two or more steps. For example, in the preparation of the magnetic layer forming composition, it is preferable that the abrasive and the ferromagnetic powder are separately dispersed. In the kneading step, an open kneader, a continuous kneader, a pressure kneader, or a kneader having a strong kneading force such as an extruder is preferably used. The details of the kneading processes of these kneaders are disclosed in JP1989-106338A (JP-H01-106338A) and JP1989-79274A (JP-H01-79274A). In addition, in order to disperse each layer forming composition, glass beads and/or other beads can be used. As such dispersion beads, zirconia beads, titania beads, and steel beads which are dispersion beads having high specific gravity are suitable. These dispersion beads are preferably used by optimizing a bead diameter and a filling percentage. As a dispersion device, a well-known dispersion device can be used.

Coating Step, Cooling Step, Heating and Drying Step, Burnishing Treatment Step, and Curing Step

The magnetic layer can be formed by directly applying the magnetic layer forming composition onto the non-magnetic support or preferably by performing multilayer coating of the magnetic layer forming composition with the non-magnetic layer forming composition in order or at the same time. For details of the coating for forming each layer, a description disclosed in a paragraph 0066 of JP2010-231843A can be referred to.

In a preferred aspect, a magnetic layer can be formed through a magnetic layer forming step including a coating step of applying a magnetic layer forming composition including ferromagnetic powder, a binder, a curing agent, and a solvent onto a non-magnetic support directly or with another layer interposed therebetween, to form a coating layer, a heating and drying step of drying the coating layer by a heating process, and a curing step of performing a curing process with respect to the coating layer. The magnetic layer forming step preferably includes a cooling step of cooling the coating layer between the coating step and the heating and drying step, and more preferably includes a burnishing treatment step of performing a burnishing treatment with respect to the surface of the coating layer between the heating and drying step and the curing step.

The inventors have thought that it is preferable that the cooling step and the burnishing treatment step in the magnetic layer forming step, in order to set the logarithmic decrement to be equal to or smaller than 0.050. More specific description is as follows.

The inventors have surmised that performing the cooling step of cooling the coating layer between the coating step and the heating and drying step contributes viscous component separated from the magnetic tape when the servo write head comes into contact with and slides on the surface of the magnetic layer, which is localized in the surface and/or a surface layer part in the vicinity of the surface of the coating layer. The inventors have surmised that this is because the viscous component at the time of solvent volatilization in the heating and drying step is easily moved to the surface and/or the surface layer part of the coating layer, by cooling the coating layer of the magnetic layer forming composition before the heating and drying step. However, the reason thereof is not clear. In addition, the inventors have thought that the viscous component can be removed by performing the burnishing treatment with respect to the surface of the coating layer in which the viscous component is localized on the surface and/or surface layer part. The inventors have surmised that performing the curing step after removing the viscous component contributes setting the logarithmic decrement to be equal to or smaller than 0.050. However, this is merely a surmise, and the invention is not limited thereto.

As described above, multilayer coating of the magnetic layer forming composition can be performed with the non-magnetic layer forming composition in order or at the same time. In a preferred aspect, the magnetic tape can be manufactured by successive multilayer coating. A manufacturing step including the successive multilayer coating can be preferably performed as follows. The non-magnetic layer is formed through a coating step of applying a non-magnetic layer forming composition onto a non-magnetic support to form a coating layer, and a heating and drying step of drying the formed coating layer by a heating process. In addition, the magnetic layer is formed through a coating step of applying a magnetic layer forming composition onto the formed non-magnetic layer to form a coating layer, and a heating and drying step of drying the formed coating layer by a heating process.

Hereinafter, a specific aspect of the manufacturing method of the magnetic tape will be described with reference to FIG. 6. However, the invention is not limited to the following specific aspect.

FIG. 6 is a step schematic view showing a specific aspect of a step of manufacturing the magnetic tape including a non-magnetic layer and a magnetic layer in this order on one surface of a non-magnetic support and including a back coating layer on the other surface thereof. In the aspect shown in FIG. 6, an operation of sending a non-magnetic support (elongated film) from a sending part and winding the non-magnetic support around a winding part is continuously performed, and various processes of coating, drying, and orientation are performed in each part or each zone shown in FIG. 6, and thus, it is possible to sequentially form a non-magnetic layer and a magnetic layer on one surface of the running non-magnetic support by multilayer coating and to form a back coating layer on the other surface thereof. Such a manufacturing method can be set to be identical to the manufacturing method normally performed for manufacturing a coating type magnetic recording medium, except for including a cooling zone in the magnetic layer forming step and including the burnishing treatment step before the curing process.

The non-magnetic layer forming composition is applied onto the non-magnetic support sent from the sending part in a first coating part (coating step of non-magnetic layer forming composition).

After the coating step, in a first heating process zone, the coating layer of the non-magnetic layer forming composition formed in the coating step is heated after to dry the coating layer (heating and drying step). The heating and drying step can be performed by causing the non-magnetic support including the coating layer of the non-magnetic layer forming composition to pass through the heated atmosphere. An atmosphere temperature of the heated atmosphere here can be, for example, approximately 60° C. to 140° C. Here, the atmosphere temperature may be a temperature at which the solvent is volatilized and the coating layer is dried, and the atmosphere temperature is not limited to the range described above. In addition, the heated air may blow to the surface of the coating layer. The points described above are also applied to a heating and drying step of a second heating process zone and a heating and drying step of a third heating process zone which will be described later, in the same manner.

Next, in a second coating part, the magnetic layer forming composition is applied onto the non-magnetic layer formed by performing the heating and drying step in the first heating process zone (coating step of magnetic layer forming composition).

After the coating step, a coating layer of the magnetic layer forming composition formed in the coating step is cooled in a cooling zone (cooling step). For example, it is possible to perform the cooling step by allowing the non-magnetic support on which the coating layer is formed on the non-magnetic layer to pass through a cooling atmosphere. An atmosphere temperature of the cooling atmosphere is preferably in a range of −10° C. to 0° C. and more preferably in a range of −5° C. to 0° C. The time for performing the cooling step (for example, time while an arbitrary part of the coating layer is delivered to and sent from the cooling zone (hereinafter, also referred to as a “staying time”)) is not particularly limited. When the staying time is long, the value of logarithmic decrement tends to be increased. Thus, the staying time is preferably adjusted by performing preliminary experiment if necessary, so that the logarithmic decrement equal to or smaller than 0.050 is realized. In the cooling step, cooled air may blow to the surface of the coating layer.

After that, while the coating layer of the magnetic layer forming composition is wet, an orientation process of the ferromagnetic powder in the coating layer is performed in an orientation zone. For the orientation process, a description disclosed in a paragraph 0067 of JP2010-231843A can be referred to.

The coating layer after the orientation process is subjected to the heating and drying step in the second heating process zone.

Next, in the third coating part, a back coating layer forming composition is applied to a surface of the non-magnetic support on a side opposite to the surface where the non-magnetic layer and the magnetic layer are formed, to form a coating layer (coating step of back coating layer forming composition). After that, the coating layer is heated and dried in the third heating process zone.

By doing so, it is possible to obtain the magnetic tape including the coating layer of the magnetic layer forming composition heated and dried on the non-magnetic layer, on one surface side of the non-magnetic support, and the back coating layer on the other surface side thereof. The magnetic tape obtained here becomes a magnetic tape product after performing various processes which will be described later.

The obtained magnetic tape is wound around the winding part, and cut (slit) to have a size of a magnetic tape product. The slitting is performed by using a well-known cutter.

In the slit magnetic tape, the burnishing treatment is performed with respect to the surface of the heated and dried coating layer of the magnetic layer forming composition, before performing the curing process (heating and light irradiation) in accordance with the types of the curing agent included in the magnetic layer forming composition (burnishing treatment step between heating and drying step and curing step). The inventors have surmised that removing the viscous component transitioned to the surface and/or the surface layer part of the coating layer cooled in the cooling zone by the burnishing treatment contributes setting the logarithmic decrement to be equal to or smaller than 0.050. However, as described above, this is merely a surmise, and the invention is not limited thereto.

The burnishing treatment is treatment of rubbing a surface of a treatment target with a member (for example, a polishing tape, or a grinding tool such as a grinding blade or a grinding wheel), and can be performed in the same manner as the well-known burnishing treatment for manufacturing a coating type magnetic recording medium. However, in the related art, the burnishing treatment was not performed in a stage before the curing step, after performing the cooling step and the heating and drying step. With respect to this, the logarithmic decrement can be equal to or smaller than 0.050 by performing the burnishing treatment in the stage described above. This point was newly found by the inventors.

The burnishing treatment can be preferably performed by performing one or both of rubbing of the surface of the coating layer of the treatment target by a polishing tape (polishing) and rubbing of the surface of the coating layer of the treatment target by a grinding tool (grinding). In a case where the magnetic layer forming composition includes an abrasive, it is preferable to use a polishing tape including at least one kind of an abrasive having higher Mohs hardness than that of the abrasive described above. As the polishing tape, a commercially available product may be used and a polishing tape manufactured by a well-known method may be used. As the grinding tool, a well-known blade such as a fixed blade, a diamond wheel, or a rotary blade, or a grinding blade can be used. In addition, a wiping treatment of wiping the surface of the coating layer rubbed by the polishing tape and/or the grinding tool with a wiping material. For details of preferred polishing tape, grinding tool, burnishing treatment, and wiping treatment, descriptions disclosed in paragraphs 0034 to 0048, FIG. 1 and Examples of JP1994-52544A (JP-1106-52544A) can be referred to. As the burnishing treatment is reinforced, the value of the logarithmic decrement tends to be decreased. The burnishing treatment can be reinforced as an abrasive having high hardness is used as the abrasive included in the polishing tape, and can be reinforced, as the amount of the abrasive in the polishing tape is increased. In addition, the burnishing treatment can be reinforced as a grinding tool having high hardness is used as the grinding tool. In regards to the burnishing treatment conditions, the burnishing treatment can be reinforced as a sliding speed between the surface of the coating layer of the treatment target and a member (for example, a polishing tape or a grinding tool) is increased. The sliding speed can be increased by increasing one or both of a speed at which the member is moved, and a speed at which the magnetic tape of the treatment target is moved.

After the burnishing treatment (burnishing treatment step), the curing process is performed with respect to the coating layer of the magnetic layer forming composition. In the aspect shown in FIG. 6, the coating layer of the magnetic layer forming composition is subjected to the surface smoothing treatment, after the burnishing treatment and before the curing process. The surface smoothing treatment is preferably performed by a calender process. For details of the calender process, for example, description disclosed in a paragraph 0026 of JP2010-231843A can be referred to. As the calender process is reinforced, the surface of the magnetic tape can be smoothened. The calender process is reinforced, as the surface temperature (calender temperature) of a calender roll is increased and/or as calender pressure is increased.

After that, the curing process according to the type of the curing agent included in the coating layer is performed with respect to the coating layer of the magnetic layer forming composition (curing step). The curing process can be performed by the process according to the type of the curing agent included in the coating layer, such as a heating process or light irradiation. The curing process conditions are not particularly limited, and the curing process conditions may be suitably set in accordance with the list of the magnetic layer forming composition used in the coating layer formation, the type of the curing agent, and the thickness of the coating layer. For example, in a case where the coating layer is formed by using the magnetic layer forming composition including polyisocyanate as the curing agent, the curing process is preferably the heating process. In a case where the curing agent is included in a layer other than the magnetic layer, a curing reaction of the layer can also be promoted by the curing process here. Alternatively, the curing step may be separately provided. After the curing step, the burnishing treatment may be further performed.

As described above, it is possible to obtain a magnetic tape having logarithmic decrement equal to or smaller than 0.050 which is acquired by pendulum viscoelasticity test performed regarding the surface of the magnetic layer of the magnetic tape. However, the manufacturing method described above is merely an example, the logarithmic decrement equal to or smaller than 0.050 can be realized by an arbitrary method capable of adjusting the logarithmic decrement, and such an aspect is also included in the invention.

Formation of Servo Pattern

The magnetic tape includes a timing-based servo pattern in the magnetic layer. FIG. 1 shows a disposition example of a region (servo band) in which the timing-based servo pattern is formed and a region (data band) interposed between two servo bands. FIG. 2 shows a disposition example of the timing-based servo patterns. Here, the disposition example shown in each drawing is merely an example, and the servo pattern, the servo bands, and the data bands may be disposed in the disposition according to a system of the magnetic tape device (drive). In addition, for the shape and the disposition of the timing-based servo pattern, a well-known technology such as disposition examples shown in FIG. 4, FIG. 5, FIG. 6, FIG. 9, FIG. 17, and FIG. 20 of U.S. Pat. No. 5,689,384A can be applied without any limitation, for example.

The servo pattern can be formed by magnetizing a specific region of the magnetic layer by a servo write head mounted on a servo writer. A region to be magnetized by the servo write head (position where the servo pattern is formed) is determined by standards. As the servo writer, a commercially available servo writer or a servo writer having a well-known configuration can be used. For the configuration of the servo writer, well-known technologies such as technologies disclosed in JP2011-175687A, U.S. Pat. Nos. 5,689,384A, and 6,542,325B can be referred to without any limitation.

The magnetic tape according to one aspect of the invention described above is a magnetic tape in which the total thickness of a non-magnetic layer and a magnetic layer is equal to or smaller than 0.60 μm and servo patterns are formed in the magnetic layer, and can prevent the output decrease of the servo signal of the timing-based servo system.

Magnetic Tape Device

One aspect of the invention relates to a magnetic tape device including the magnetic tape, a magnetic head, and a servo head.

The details of the magnetic tape mounted on the magnetic tape device are as described above. The magnetic tape is generally accommodated in a magnetic tape cartridge and the magnetic tape cartridge is attached to the magnetic tape device. Details of the structure of the magnetic tape cartridge are well known. The magnetic tape cartridge is mounted on the magnetic tape device. The magnetic tape includes timing-based servo patterns. Accordingly, a magnetic signal is recorded on the data band by the magnetic head to form a data track, and/or, when reproducing the recorded signal, a head tracking of a timing-based servo type can be performed based on the read servo pattern, while reading the servo pattern by the servo head. Here, when the output of the servo signal is decreased, the head positioning accuracy may be decreased, as described above. With respect to this, according to the magnetic tape, it is possible to prevent the output decrease of the servo signal, and accordingly, it is possible to cause the magnetic head to follow the data track at a high accuracy in the timing-based servo system.

As the magnetic head mounted on the magnetic tape device, a well-known magnetic head which can perform the recording and/or reproducing of the magnetic signal with respect to the magnetic tape can be used. A recording head and a reproduction head may be one magnetic head or may be separated magnetic heads. As the servo head, a well-known servo head which can read the timing-based servo pattern of the magnetic tape can be used. At least one or two or more servo heads may be included in the magnetic tape device.

For details of the head tracking of the timing-based servo system, for example, well-known technologies such as technologies disclosed in U.S. Pat. Nos. 5,689,384A, 6,542,325B, and 7,876,521B can be used without any limitation.

A commercially available magnetic tape device generally includes a magnetic head and a servo head in accordance to a standard. In addition, a commercially available magnetic tape device generally has a servo controlling mechanism for realizing head tracking of the timing-based servo system in accordance to a standard. The magnetic tape device according to one aspect of the invention can be configured by incorporating the magnetic tape according to one aspect of the invention to a commercially available magnetic tape device.

EXAMPLES

Hereinafter, the invention will be described with reference to Examples. However, the invention is not limited to aspects shown in the Examples. “Parts” and “%” in the following description mean “parts by mass” and “mass %”, unless otherwise noted.

Examples 1 to 7 and Comparative Examples 1 to 6

1. Preparation of Alumina Dispersion

3.0 parts of 2,3-dihydroxynaphthalene (manufactured by Tokyo Chemical Industry Co., Ltd.), 31.3 parts of a 32% solution (solvent is a mixed solvent of methyl ethyl ketone and toluene) of a polyester polyurethane resin having a SO₃Na group as a polar group (UR-4800 (amount of a polar group: 80 meq/kg) manufactured by Toyobo Co., Ltd.), and 570.0 parts of a mixed solution of methyl ethyl ketone and cyclohexanone (mass ratio of 1:1) as a solvent were mixed in 100.0 parts of alumina powder (HIT-80 manufactured by Sumitomo Chemical Co., Ltd.) having an gelatinization ratio of 65% and a BET specific surface area of 20 m²/g, and dispersed in the presence of zirconia beads by a paint shaker for 5 hours. After the dispersion, the dispersion liquid and the beads were separated by a mesh and an alumina dispersion was obtained.

2. Magnetic Layer Forming Composition List

Magnetic Solution

Ferromagnetic powder: see Table 1: 100.0 parts

SO₃Na group-containing polyurethane resin: 14.0 parts

Weight-average molecular weight: 70,000, SO₃Na group: 0.2 meq/g

Cyclohexanone: 150.0 parts

Methyl ethyl ketone: 150.0 parts

Abrasive liquid

Alumina dispersion prepared in the section 1.: 6.0 parts

Silica Sol

Colloidal silica

Average particle size: 80 nm: 2.0 parts

Methyl ethyl ketone: 1.4 parts

Other Components

Stearic acid: 2.0 parts

Stearic acid amide: 0.2 parts

Butyl stearate: 2.0 parts

Polyisocyanate (CORONATE (registered trademark) L manufactured by Nippon Polyurethane Industry): 2.5 parts

Finishing Additive Solvent

Cyclohexanone: 200.0 parts

Methyl ethyl ketone: 200.0 parts

In Table 1, BF indicates ferromagnetic hexagonal barium ferrite powder having an average particle size (average plate diameter) of 21 nm, and MP indicates ferromagnetic metal powder having an average particle size (average long axis length) of 30 nm.

3. Non-Magnetic Layer Forming Composition List

Non-magnetic inorganic powder: α-iron oxide: 100.0 parts

Average particle size (average long axis length): 0.15 μm

Average acicular ratio: 7

BET specific surface area: 52 m²/g

Carbon black: 20.0 parts

Average particle size: 20 nm

Vinyl chloride copolymer: 13.0 parts

SO₃Na group-containing polyurethane resin: 9.0 parts

Weight-average molecular weight: 70,000, SO₃Na group: 0.2 meq/g

Phenylphosphonic acid: 3.0 parts

Stearic acid: 2.0 parts

Stearic acid amide: 0.2 parts

Butyl stearate: 2.0 parts

Cyclohexanone: 300.0 parts

Methyl ethyl ketone: 300.0 parts

4. Back Coating Layer Forming Composition List

Non-magnetic inorganic powder: α-iron oxide: 80.0 parts

Average particle size (average long axis length): 0.15 μm

Average acicular ratio: 7

BET specific surface area: 52 m²/g

Carbon black: 20.0 parts

Average particle size: 20 nm

Vinyl chloride copolymer: 13.0 parts

SO₃Na group-containing polyurethane resin: 6.0 parts

Phenylphosphonic acid: 3.0 parts

Methyl ethyl ketone: 155.0 parts

Stearic acid: 3.0 parts

Butyl stearate: 3.0 parts

Polyisocyanate: 5.0 parts

Cyclohexanone: 355.0 parts

5. Preparation of Each Layer Forming Composition

The magnetic layer forming composition was prepared by the following method. The magnetic solution was prepared by dispersing (beads-dispersing) each component with a batch type vertical sand mill for 24 hours. As the dispersion beads, zirconia beads having a bead diameter of 0.1 mm were used. The prepared magnetic solution and the abrasive liquid were mixed with other components (silica sol, other components, and finishing additive solvent) and beads-dispersed for 5 minutes by using the sand mill, and a process (ultrasonic dispersion) was performed with a batch type ultrasonic device (20 kHz, 300 W) for 0.5 minutes. After that, the filtering was performed by using a filter having an average hole diameter of 0.5 μm, and the magnetic layer forming composition was prepared.

The non-magnetic layer forming composition was prepared by the following method. Each component excluding a lubricant (stearic acid, stearic acid amide, and butyl stearate), cyclohexanone, and methyl ethyl ketone was dispersed by using batch type vertical sand mill for 24 hours to obtain dispersion liquid. As the dispersion beads, zirconia beads having a bead diameter of 0.1 mm were used. After that, the remaining components were added into the obtained dispersion liquid and stirred with a dissolver. The dispersion liquid obtained as described above was filtered with a filter having an average hole diameter of 0.5 μm and a non-magnetic layer forming composition was prepared.

The back coating layer forming composition was prepared by the following method. Each component excluding the lubricant (stearic acid and butyl stearate), polyisocyanate, and cyclohexanone was kneaded and diluted by an open kneader, and subjected to a dispersing process of 12 passes, with a transverse beads mill dispersion device and zirconia beads having a bead diameter of 1 mm, by setting a bead filling percentage as 80 volume %, a circumferential speed of rotor tip as 10 m/sec, and a retention time for 1 pass as 2 minutes. After that, the remaining components were added into the obtained dispersion liquid and stirred with a dissolver. The dispersion liquid obtained as described above was filtered with a filter having an average hole diameter of 1 μm and a back coating layer forming composition was prepared.

6. Manufacturing of Magnetic Tape in which Servo Patterns are Formed

The magnetic tape was manufactured by a specific aspect shown in FIG. 6. The magnetic tape was specifically manufactured as follows.

A support made of polyethylene naphthalate having a thickness shown in Table 1 was sent from the sending part, and the non-magnetic layer forming composition prepared in the section 5. was applied to one surface thereof so that the thickness after the drying becomes the thickness shown in Table 1 in the first coating part and was dried in the first heating process zone (atmosphere temperature of 100° C.) to form a coating layer.

Then, the magnetic layer forming composition prepared in the section 5. was applied onto the non-magnetic layer so that the thickness after the drying became the thickness shown in Table 1 in the second coating part, and a coating layer was formed. The cooling step was performed by passing the formed coating layer through the cooling zone in which the atmosphere temperature is adjusted to 0° C. for the staying time shown in Table 1 while the coating layer is wet, a vertical alignment process was performed in the orientation zone by applying a magnetic field having a magnetic field strength of 0.3 T in a vertical direction, and then, the coating layer was dried in the second heating process zone (atmosphere temperature of 100° C.) at an atmosphere temperature of 100° C.

After that, in the third coating part, the back coating layer forming composition prepared in the section 5. was applied to the surface of the support made of polyethylene naphthalate on a side opposite to the surface where the non-magnetic layer and the magnetic layer were formed, so that the thickness after the drying became the thickness shown in Table 1, to form a coating layer, and the formed coating layer was dried in the third heating process zone (atmosphere temperature of 100° C.).

The magnetic tape obtained as described above was slit to have a width of ½ inches (0.0127 meters), and the burnishing treatment and the wiping treatment were performed with respect to the surface of the coating layer of the magnetic layer forming composition. The burnishing treatment and the wiping treatment were performed by using a commercially available polishing tape (product name: MA22000 manufactured by Fujifilm Holdings Corporation, abrasive: diamond/Cr₂O₃/red oxide) as the polishing tape, a commercially available sapphire blade (manufactured by Kyocera Corporation, a width of 5 mm, a length of 35 mm, and a tip angle of 60 degrees) as the grinding blade, and a commercially available wiping material (product name: WRP736 manufactured by Kuraray Co., Ltd) as the wiping material, in a treatment device having a configuration disclosed in FIG. 1 of JP1994-52544A (JP-1106-52544A). For the treatment conditions, the treatment conditions disclosed in Example 12 of JP1994-52544A (JP-1106-52544A).

After the burnishing treatment and the wiping treatment, a calender process (surface smoothing treatment) was performed with a calender roll configured of only a metal roll, at a speed of 80 m/min, linear pressure of 300 kg/cm (294 kN/m), and a surface temperature of a calender roll of 95° C.

Then, the curing process (heating process) was performed in the environment of the atmosphere temperature of 70° C. for 36 hours to obtain a magnetic tape.

In Table 1, in the Comparative Examples in which “not performed” is disclosed in a column of the cooling zone staying time, a magnetic tape was manufactured by a manufacturing step not including a cooling zone.

In Table 1, in the Comparative Examples in which “not performed” is disclosed in a column of the burnishing treatment before the curing step, a magnetic tape was manufactured by a manufacturing step of not performing the burnishing treatment and the subsequent wiping treatment in the step before performing the curing process.

In Table 1, in Comparative Example 6 in which “performed” is disclosed in a column of the burnishing treatment before the curing step, the burnishing treatment and the wiping treatment described above were continuously repeated 10 times in the step after performing the curing process.

By performing the steps described above, the magnetic tape was manufactured.

7. Formation of Timing-Based Servo Pattern

In a state where the magnetic layer of the manufactured magnetic tape was demagnetized, servo patterns having disposition and shapes according to the LTO Ultrium format were formed on the magnetic layer by using a servo write head mounted on a servo testing machine. Accordingly, a magnetic tape including data bands, servo bands, and guide bands in the disposition according to the LTO Ultrium format in the magnetic layer, and including servo patterns having the disposition and the shape according to the LTO Ultrium format on the servo band is obtained. In this magnetic tape, total 5,000,000 servo frames of servo frames including the A burst, B burst, C burst, and D burst are formed in the disposition shown in FIG. 2. The servo testing machine includes a servo write head and a servo head. This servo testing machine was also used in the evaluation which will be described later.

By performing the steps described above, each magnetic tape of Examples and Comparative Examples in which a timing-based servo pattern is formed in a magnetic layer was obtained. The following evaluation of the obtained each magnetic tape was performed.

The thickness of each layer and the non-magnetic support of each magnetic tape obtained as described above was acquired by the following method. It was confirmed that each layer and the non-magnetic support formed have the thickness shown in Table 1.

The cross section of the magnetic tape in a thickness direction was exposed by an ion beam, and then, the cross section observation of the exposed cross section was performed with a scanning electron microscope. Various thicknesses were acquired as an arithmetical mean of thicknesses acquired at two positions in the thickness direction, in the cross section observation.

Evaluation Method

1. Measurement of Logarithmic Decrement

The logarithmic decrement of the surface of the magnetic layer of each magnetic tape of Examples and Comparative Examples was acquired by the method described above by using a rigid-body pendulum type physical properties testing instrument RPT-3000W (pendulum: brass, substrate: glass substrate, a rate of temperature increase of substrate: 5° C./min) as the measurement device. A measurement sample cut out from each magnetic tape of Examples and Comparative Examples was placed on a glass substrate having a size of approximately 3 cm×approximately 5 cm, by being fixed at 4 portions with a fixing tape (Kapton tape manufactured by Du Pont-Toray Co., Ltd.) as shown in FIG. 3. An adsorption time was set as 1 second, a measurement interval was set as 7 to 10 seconds, a displacement-time curve was drawn regarding the 86-th measurement interval, and the logarithmic decrement was acquired by using this curve. The measurement was performed in the environment of relative humidity of approximately 50%.

2. Output Decreased Amount of Servo Signal

The magnetic tape in which the timing-based servo pattern is formed was attached to a servo testing machine. In the servo testing machine, the servo patterns were sequentially read (servo signals were reproduced) by the servo head from the servo pattern of the first servo frame formed in the magnetic tape to the servo pattern of the final 5,000,000-th servo frame, while bringing the surface of the magnetic layer of the running magnetic tape to come into contact with and slide on the servo head. An arithmetical mean of the signal output obtained in the first to 100-th servo frames was set as A, an arithmetical mean of the signal output obtained in the 4,999,900-th to 5,000,000-th servo frames was set as B, and the output decreased amount of the servo signal (unit: %) was calculated with an expression of “[(B−A)/A]×100”.

The results described above are shown in Table 1.

TABLE 1 Comparative Comparative Comparative Comparative Comparative Comparative Example Example 1 Example 2 Example 3 Example 4 Example 5 Example 6 1 Ferromagnetic powder BF BF BF BF MP BF BF Magnetic layer thickness μm 0.10 0.10 0.10 0.10 0.10 0.10 0.10 Non-magnetic layer μm 1.00 0.70 0.50 0.10 0.50 0.50 0.50 thickness Non-magnetic support μm 4.30 4.30 4.30 4.30 4.30 4.30 4.30 thickness Back coating layer μm 0.60 0.60 0.60 0.60 0.60 0.60 0.60 thickness Total thickness of μm 1.10 0.80 0.60 0.20 0.60 0.60 0.60 non-magnetic layer + magnetic layer Cooling zone staying Not Not Not Not Not Not 1 second time performed performed performed performed performed performed Burnishing treatment Not Not Not Not Not Not Performed before curing step performed performed performed performed performed performed Burnishing treatment Not Not Not Not Not Performed Not after curing step performed performed performed performed performed performed Logarithmic decrement 0.062 0.061 0.062 0.063 0.072 0.056 0.048 of magnetic layer Servo signal output % −0.30 −0.60 −2.80 −43.00 −8.20 −3.40 −1.00 decreased amount Example Example Example Example Example Example 2 3 4 5 6 7 Ferromagnetic powder BF BF BF BF MP BF Magnetic layer thickness μm 0.10 0.10 0.10 0.10 0.10 0.10 Non-magnetic layer μm 0.50 0.50 0.50 0.50 0.50 0.10 thickness Non-magnetic support μm 4.30 4.30 4.30 4.30 4.30 4.30 thickness Back coating layer μm 0.60 0.60 0.60 0.60 0.60 0.60 thickness Total thickness of μm 0.60 0.60 0.60 0.60 0.60 0.20 non-magnetic layer + magnetic layer Cooling zone staying 5 seconds 60 seconds 120 seconds 180 seconds 5 seconds 5 seconds time Burnishing treatment Performed Performed Performed Performed Performed Performed before curing step Burnishing treatment Not Not Not Not Not Not after curing step performed performed performed performed performed performed Logarithmic decrement 0.042 0.034 0.021 0.015 0.045 0.043 of magnetic layer Servo signal output % −0.70 −0.05 −0.10 −0.10 −0.90 −0.80 decreased amount

With the comparison of Comparative Examples, it was confirmed that, in the case where the total thickness of the non-magnetic layer and the magnetic layer is equal to or smaller than 0.60 μm (Comparative Examples 3 to 6), the output of the servo signal is significantly decreased, compared to the case where the total thickness of the non-magnetic layer and the magnetic layer exceeds 0.60 μm (Comparative Examples 1 and 2).

With respect to this, in the magnetic tape of Examples 1 to 7, the total thickness of the non-magnetic layer and the magnetic layer is equal to or smaller than 0.60 μm, however, the output decrease of the servo signal was prevented, compared to that of the magnetic tape of Comparative Examples 3 to 6.

An aspect of the invention can be effective in technical fields of magnetic tapes for high-density recording.

EXPLANATION OF REFERENCES

-   -   1: MAGNETIC TAPE     -   10: SERVO BAND     -   11: DATA BAND     -   12: GUIDE BAND     -   SF: SERVO FRAME     -   SSF: SERVO SUB-FRAME     -   A: A BURST     -   A1 to A5: SERVO PATTERN     -   B: B BURST     -   B1 to B5: SERVO PATTERN     -   C: C BURST     -   C1 to C4: SERVO PATTERN     -   D: D BURST     -   D1 to D4: SERVO PATTERN     -   100: MEASUREMENT SAMPLE     -   101: SAMPLE STAGE     -   102: HOLDER AND TEMPERATURE SENSOR     -   103: SUBSTRATE     -   104: COLUMNAR CYLINDER EDGE     -   105: FIXING TAPE     -   106: MAGNET (FOR INDUCTION OF INITIAL VIBRATION)     -   107: PENDULUM     -   108: DISPLACEMENT SENSOR 

What is claimed is:
 1. A magnetic tape comprising: a non-magnetic support; a non-magnetic layer including non-magnetic powder and a binder on the non-magnetic support; and a magnetic layer including ferromagnetic powder and a binder on the non-magnetic layer, wherein the total thickness of the non-magnetic layer and the magnetic layer is equal to or smaller than 0.60 μm, the magnetic layer includes a timing-based servo pattern, the logarithmic decrement acquired by a pendulum viscoelasticity test performed regarding the surface of the magnetic layer within a range of 0.010 to 0.050, and the logarithmic decrement on the magnetic layer side is determined by the following method; securing a measurement sample of the magnetic tape with the measurement surface, which is the surface on the magnetic layer side, facing upward on a substrate in a pendulum viscoelasticity tester; disposing a columnar cylinder edge which is 4 mm in diameter and equipped with a pendulum 13 g in weight on the measurement surface of the measurement sample such that the long axis direction of the columnar cylinder edge runs parallel to the longitudinal direction of the measurement sample; raising the surface temperature of the substrate on which the measurement sample has been positioned at a rate of less than or equal to 5° C./min up to 80° C.; inducing initial oscillation of the pendulum; monitoring the displacement of the pendulum while it is oscillating to obtain a displacement-time curve for a measurement interval of greater than or equal to 10 minutes; and obtaining the logarithmic decrement Δ from the following equation: $\Delta = \frac{{\ln\left( \frac{A_{1}}{A_{2\;}} \right)} + {\ln\left( \frac{A_{2}}{A_{3}} \right)} + {\ldots\mspace{14mu}{\ln\left( \frac{A_{n}}{A_{n + 1}} \right)}}}{n}$ wherein the interval from one minimum displacement to the next minimum displacement is adopted as one wave period; the number of waves contained in the displacement-time curve during one measurement interval is denoted by n, the difference between the minimum displacement and the maximum displacement of the n^(th) wave is denoted by An, and the logarithmic decrement is calculated using the difference between the next minimum displacement and maximum displacement of the n^(th) wave (A_(n+1) in the above equation).
 2. The magnetic tape according to claim 1, wherein the logarithmic decrement is 0.010 to 0.040.
 3. The magnetic tape according to claim 2, wherein the total thickness of the non-magnetic layer and the magnetic layer is 0.20 μm to 0.60 μm.
 4. The magnetic tape according to claim 1, wherein the total thickness of the non-magnetic layer and the magnetic layer is 0.20 μm to 0.60 μm.
 5. A magnetic tape device comprising: a magnetic tape, a magnetic head; and a servo head, wherein the magnetic tape is a magnetic tape comprising: a non-magnetic support; a non-magnetic layer including non-magnetic powder and a binder on the non-magnetic support; and a magnetic layer including ferromagnetic powder and a binder on the non-magnetic layer, wherein the total thickness of the non-magnetic layer and the magnetic layer is equal to or smaller than 0.60 μm, the magnetic layer includes a timing-based servo pattern, the logarithmic decrement acquired by a pendulum viscoelasticity test performed regarding the surface of the magnetic layer is within a range of 0.010 to 0.050, and the logarithmic decrement on the magnetic layer side is determined by the following method; securing a measurement sample of the magnetic tape with the measurement surface, which is the surface on the magnetic layer side, facing upward on a substrate in a pendulum viscoelasticity tester; disposing a columnar cylinder edge which is 4 mm in diameter and equipped with a pendulum 13 g in weight on the measurement surface of the measurement sample such that the long axis direction of the columnar cylinder edge runs parallel to the longitudinal direction of the measurement sample; raising the surface temperature of the substrate on which the measurement sample has been positioned at a rate of less than or equal to 5° C./min up to 80° C.; inducing initial oscillation of the pendulum; monitoring the displacement of the pendulum while it is oscillating to obtain a displacement-time curve for a measurement interval of greater than or equal to 10 minutes; and obtaining the logarithmic decrement Δ from the following equation: $\Delta = \frac{{\ln\left( \frac{A_{1}}{A_{2\;}} \right)} + {\ln\left( \frac{A_{2}}{A_{3}} \right)} + {\ldots\mspace{14mu}{\ln\left( \frac{A_{n}}{A_{n + 1}} \right)}}}{n}$ wherein the interval from one minimum displacement to the next minimum displacement is adopted as one wave period; the number of waves contained in the displacement-time curve during one measurement interval is denoted by n, the difference between the minimum displacement and the maximum displacement of the n^(th) wave is denoted by An, and the logarithmic decrement is calculated using the difference between the next minimum displacement and maximum displacement of the n^(th) wave (A_(n+1) in the above equation).
 6. The magnetic tape device according to claim 5, wherein the logarithmic decrement is 0.010 to 0.040.
 7. The magnetic tape device according to claim 6, wherein the total thickness of the non-magnetic layer and the magnetic layer of the magnetic tape is 0.20 μm to 0.60 μm.
 8. The magnetic tape device according to claim 5, wherein the total thickness of the non-magnetic layer and the magnetic layer of the magnetic tape is 0.20 μm to 0.60 μm. 